德國朗盛LANXESS Durethan PA6 BKV135是一種加35%玻璃纖維，注塑，提高流動性，表面光潔度，低翹曲傾向樹脂，尼龍從環(huán)境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV135

生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)BKV135/德國朗盛/物性表參數(shù)

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 290 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.3
	Molding shrinkage, transverse	150x105x3; 290 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.9
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	10200	6000
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	170	110
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	7.0
	Tensile creep modulus	1 h	MPa	ISO 899-1		4800
	Tensile creep modulus	1000 h	MPa	ISO 899-1		3800
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	100	110
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	85	85
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	20	30
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	10
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	20	28
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	15	15
	Flexural modulus	2 mm/min	MPa	ISO 178-A	9100	5500
	Flexural strength	2 mm/min	MPa	ISO 178-A	280	170
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	260	140
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	213
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	22
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 200
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.0	10
	Relative permittivity	1 MHz	-	IEC 60250	4.0	5.0
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
	Surface resistivity		Ohm	IEC 60093	1E14	1E12
	Electric strength	1 mm	kV/mm	IEC 60243-1	40	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.5
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.8
	Density		kg/m³	ISO 1183	1410
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-290
	Mold temperature		°C	-	80-100

溫馨提示：
本物性表參數(shù)提供者不承擔任何法律責任，建議在選擇材料前，就數(shù)據(jù)值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯(lián)系.

上一頁：PA6(尼龍6)BG30XXF/德國朗盛/物性表參數(shù) 下一頁：PA6(尼龍6)BKV140/德國朗盛/物性表參數(shù)