PA6(尼龍6)BKV215H3.0/德國朗盛/物性表參數

日期：2020-04-25 02:25:16 編輯：科思德塑膠來源：科思德塑膠瀏覽：248

德國朗盛LANXESS Durethan PA6 BKV215H3.0是一種加15%玻璃纖維，注塑，提高流動性，表面光潔度，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。

生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)BKV215H3.0/德國朗盛/物性表參數

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.3
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.83
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.05
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.15
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	4500	2300
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	85	50
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	4.5	15
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	70	95
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	80	80
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	20	35
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	12
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	60	90
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	65	60
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	20	35
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	10	10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	4200	2300
	Flexural strength	2 mm/min	MPa	ISO 178-A	135	75
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.5	8.5
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	125	55
	Puncture maximum force	23 °C	N	ISO 6603-2	1000
	Puncture maximum force	-30 °C	N	ISO 6603-2	650
	Puncture energy	23 °C	J	ISO 6603-2	13
	Puncture energy	-30 °C	J	ISO 6603-2	4.8
	Ball indentation hardness		N/mm²	ISO 2039-1	110	55
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	214
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	175
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	205
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.4
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.7
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	22
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	7.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.0
	Density		kg/m³	ISO 1183	1180
	Bulk density		kg/m³	ISO 60	600
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-290
	Mold temperature		°C	-	80-100

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.

上一頁：PA6(尼龍6)BKV215H2.0/德國朗盛/物性表參數下一頁：PBT(聚對苯二甲酸丁二酯)2002K|寶理塑料|物性表參數