PA6(尼龍6)BKV25H2.0/德國朗盛/物性表參數

日期：2020-04-14 09:41:50 編輯：科思德塑膠來源：科思德塑膠瀏覽：259

德國朗盛LANXESS Durethan PA6 BKV25H2.0是一種加入25%玻璃纖維，注塑，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV25H2.0

以下是PA6(尼龍6)BKV25H2.0/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.21
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.88
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.04
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.14
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8400	5100
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	160	90
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	6.0
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	60	80
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	45	45
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10	10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Charpy notched impact strength	-40 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Izod notched impact strength	-40 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	7200	4200
	Flexural strength	2 mm/min	MPa	ISO 178-A	250	145
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	230	120
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
Other properties (23 °C)
	Density		kg/m³	ISO 1183	1320
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.