PA6(尼龍6)BKV50GH2.0EF/德國朗盛/物性表參數

日期：2020-04-14 10:00:39 編輯：科思德塑膠來源：科思德塑膠瀏覽：248

德國朗盛LANXESS Durethan PA6 BKV50GH2.0EF是一種加入50%玻璃纖維，提高表面光潔度，改善流動性，注塑，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV50GH2.0EF

以下是PA6(尼龍6)BKV50GH2.0EF/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.15
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.5
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.07
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.13
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	16500	11500
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	220	150
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3	4.5
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	15	17
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	13	12
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	90	85
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	90
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	15	18
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	15	13
	Flexural modulus	2 mm/min	MPa	ISO 178-A	15500	11000
	Flexural strength	2 mm/min	MPa	ISO 178-A	340	230
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3	4
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		220
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	220
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	204
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	219
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.151
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.714
Other properties (23 °C)
	Density		kg/m³	ISO 1183	1570
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120