PA6(尼龍6)BM230H2.0/德國朗盛/物性表參數

日期：2020-04-14 10:08:36 編輯：科思德塑膠來源：科思德塑膠瀏覽：239

德國朗盛LANXESS Durethan PA6 BM230H2.0是一種加入30%礦物纖維，注塑，低變形，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同,這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BM230H2.0

以下是PA6(尼龍6)BM230H2.0/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	1.08
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	1.12
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.32
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.3
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	5000	2000
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	80	50
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	10	45
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	120	N
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	80	80
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10	13
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Charpy notched impact strength	-40 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	122	N
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	80	95
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Izod notched impact strength	-40 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	4700	1800
	Flexural strength	2 mm/min	MPa	ISO 178-A	140	60
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.5	8.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	130	55
	Puncture maximum force	23 °C	N	ISO 6603-2	4694
	Puncture maximum force	-30 °C	N	ISO 6603-2	1132
	Puncture energy	23 °C	J	ISO 6603-2	19.1
	Puncture energy	-30 °C	J	ISO 6603-2	4.2
	Ball indentation hardness		N/mm²	ISO 2039-1	180	80
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	~70
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	~185
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	~50
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94 (1.6 mm)	1.6 mm	Class	UL 94	HB
	Burning behavior UL 94	3.2 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	25
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302			ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	200
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.3	16
	Relative permittivity	1 MHz	-	IEC 60250	3.9	4.7
	Dissipation factor	100 Hz	10-4	IEC 60250	80	3250
	Dissipation factor	1 MHz	10-4	IEC 60250	180	1100
	Volume resistivity		Ohm·m	IEC 60093	1E12	1E10
	Surface resistivity		Ohm	IEC 60093	1E16	1E13
	Electric strength	1 mm	kV/mm	IEC 60243-1	29	27
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	525 (475)
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	200 M - 0.3
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	~7.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	~2.2
	Density		kg/m³	ISO 1183	1360
	Bulk density		kg/m³	ISO 60	~800
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120