VALOX(沙伯基礎)VX4920/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX VX4920 PBT是一種加20%玻璃增強有核PBT/ASA共混物，具有優異的機械性能、高維穩性和低密度,應用領域:連接器及汽車工業。
 |
沙伯基礎創新塑料的VALOX VX4920 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)VX4920/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 105 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 105 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7200 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5500 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 80 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5700 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 130 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 118 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 40 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 680 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 605 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 70 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 8 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 170 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.25 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.86E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.67E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.05E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.38E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.57E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 165 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 209 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 179 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 170 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.38 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.4 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.4-0.8 | % | SABIC method | |
| Melt Flow Rate, 200°C/3.8 kgf | 17 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 | |
| Density | 1.38 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.76 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.27 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 17 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 175 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 24 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 24 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0024 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.4 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：12722 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：11061 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：10730 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9114 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7914 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7887 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7309 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6812 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6507 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6459 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6431 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6333 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：6148 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：6129 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力于其性能的提高和
瀏覽量：6021
推薦文章
-
塞拉尼斯TPV 281-64MED|Santoprene物性表參數
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 281-64MED是一種熱塑性硫化彈性體，TPV 281-64MED也是熱塑性彈性體(TPE)家族中的一種柔軟、可著色的特種熱塑性硫化膠(TPV)，該等級的Santoprene TPV是剪切依賴的，可以在傳統的熱塑性塑料設備上進行注射成型，擠出或吹塑加工，它是聚烯烴為基礎的，完全可回收。以下是塞拉尼斯TP
-
Zytel(塞拉尼斯)70G35HSLR|PA66(尼龍66)物性表參數
塞拉尼斯Zytel 70G35HSLR PA66是一種35% 玻纖增強, 熱穩定, 耐水解尼龍66樹脂,包括良好的機械和物理性能，例如高機械強度，剛性和韌性之間良好的平衡，良好的高溫性能、電性能和阻燃性能，優異的耐磨損和耐化學品性能。Zytel(塞拉尼斯)70G35HSLR/PA66(尼龍66)物性表參數PDF文檔下載生產商：塞拉尼斯,商品名：ZytelZytel是塞
-
LCP/T130/LCP物性表參數
日本寶理 LCP 物性表 LAPEROS T130 物性表參數 T130是Polyplastics寶理公司液晶高分子聚合物LCP型號之一,商品名LAPEROS,具有優異的自增強性、熱穩定性、耐高熱性、耐化學藥品性、耐氣候性、耐
-
PP(聚丙烯)RP340N/利安德巴塞爾/物性表參數
利安德巴塞爾(Lyondellbasell)Moplen PP RP340N是一種聚丙烯無規共聚物，具有中等熔體流動速率，用于注塑應用，熔體流動速率(230°C/2.16kg)是11克/10分鐘，密度(23°C)是0.9克/厘米3，moplen RP340N是成核的，用于提高生產率和非常好的光學性能(透明度和亮度)，它具有滿足食品工業苛刻要求的感官特征，moplen RP340N通常
-
TPU(熱塑性聚氨酯)11T93/路博潤(Lubrizol)物性表參數
路博潤(Lubrizol)Pearlthane TPU 11T93是一種以聚己內酯共聚酯為基礎的熱塑性聚氨酯，肖氏硬度93A，特點是剛性等級高，具有優異的耐化學性和耐油性，本系列旨在滿足對廣泛技術應用日益嚴格的需求，例如高柔韌性薄膜、耐磨軟管、柔軟注塑部件或特殊化合物，主要用于擠出成型應用。以下是TPU(熱塑性聚氨酯)11T93/路博潤(Lubri
-
PPS(聚苯硫醚)7140A4/寶理塑料/物性表參數
日本寶理DURAFIDE PPS 7140A4 是一種加PTFE和加30%碳纖導電，防火級別的PPS原料，簡支梁沖擊強度是4.5 kJ/m，可應用于燈座、水泵、各種電裝部件等，作為汽車部件、OA設備、AV設備的功能部件
-
PPS(聚苯硫醚)FZ-2140-D9/日本油墨DIC/物性表參數
日本油墨DIC PPS FZ-2140-D9 是一種玻璃纖維增強GF40%,高流動、低飛邊線型PPS,具有熔點約280℃的高耐熱性能及優良的耐藥品性，無需添加阻燃劑即可自熄的高阻燃性的樹脂材料,有著高度的耐
-
PC(聚碳酸酯)XHT2146/沙伯基礎(SABIC)物性表參數
沙伯基礎創新塑料（SABIC）LEXAN PC XHT2146 是一種高流動、高耐熱的聚碳酸酯共聚物，與LEXAN XHT2141樹脂相比，具有更好的釋放性能，它可在一系列不透明和有限的透明顏色。 PC(聚碳酸酯
-
PP(聚丙烯)BB120/韓華道達爾/物性表參數
韓華道達爾嵌段 PP BB120 是用于片材和吸塑用途的嵌段共聚HIPP牌號,韓華道達爾的抗沖聚丙烯具有低溫條件下優異的剛性和沖擊強度平衡性，同時具有良好的加工性能.其特點是：優異的剛
-
PC(聚碳酸酯)D251/沙伯基礎(SABIC)物性表參數
沙伯基礎(SABIC)LNP Thermocomp PC D251是一種加玻璃纖維增強聚碳酸酯樹脂，密度是1.35g/cm3，熔體流動速率(300°C/1.2 kg)是17g/10min，該材料的附加特性包括:阻燃，高模量，良好的表面，良好的平整度，良好的延展性，非溴化和非氯化阻燃。以下是PC(聚碳酸酯)D251/沙伯基礎(SABIC)物性表參數基本信息填料/增強材料玻璃纖維