PC(聚碳酸酯)SLX2071T/沙伯基礎(SABIC)物性表參數

日期：2020-06-19 02:22:34 編輯：科思德塑膠來源：科思德塑膠瀏覽：325

SABIC(沙伯基礎創新塑料)LEXAN PC SLX2071T是一種高粘度PC共聚物材料，（熔體流動速率）(300°C/1.2 kg)6.0g/10 min，增強了UV穩定性，并添加了釋放劑，阻燃V2評級，可在透明和多種顏色。

PC(聚碳酸酯)SLX2071T/沙伯基礎(SABIC)物性表參數PDF文檔下載

以下是PC(聚碳酸酯)SLX2071T/沙伯基礎(SABIC)物性表參數

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	67	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	76	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6.3	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	>100	%	ASTM D 638
Tensile Modulus, 5 mm/min	2340	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	96	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2120	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	67	MPa	ISO 527
Tensile Stress, break, 50 mm/min	76	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6.3	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Tensile Modulus, 1 mm/min	2340	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	96	MPa	ISO 178
Flexural Modulus, 2 mm/min	2120	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	820	J/m	ASTM D 256
Izod Impact, notched, -30°C	140	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	85	J	ASTM D 3763
THERMAL
Vicat Softening Temp, Rate B/50	135	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	134	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	7.E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	137	°C	ISO 306
Vicat Softening Temp, Rate B/120	139	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	121	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.2	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.5-0.7	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	6	g/10 min	ASTM D 1238
Density	1.2	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.35	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	5	cm³/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm	89	%	ASTM D 1003
Haze, 2.54 mm	0.5	%	ASTM D 1003
Profile Extrusion
Drying Temperature	105	°C
Drying Time	2-3	hrs
Melt Temperature	220-250	°C
Barrel - Zone 1 Temperature	240-280	°C
Barrel - Zone 2 Temperature	240-280	°C
Barrel - Zone 3 Temperature	220-240	°C
Barrel - Zone 4 Temperature	220-240	°C
Hopper Temperature	60-80	°C
Adapter Temperature	220-240	°C
Die Temperature	245-290	°C
Calibrator Temperature	60-100	°C

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
為及時發現和糾正網站存在的信息內容等方面問題，在使用網站時及時反饋網站問題，從而幫助推進網站信息內容建設工作，提高網站信息互動交流。

上一頁：PC(聚碳酸酯)SLX1432/沙伯基礎(SABIC)物性表參數下一頁：PC(聚碳酸酯)SLX2432T/沙伯基礎(SABIC)物性表參數

返回首頁返回物性參數列表

PC(聚碳酸酯)SLX2071T/沙伯基礎(SABIC)物性表參數

熱門文章

推薦文章